| Commodity | Austenitic, Ferritic, Martensitic, Duplex, Cold rolled, Hot rolled |
| Grade | 201, 202, 301, 304, 304j1, 304l, 321, 309s, 310s, 2205, 409l, 410, 410s, 420, 420j1, 420j2, 430, 439, 409l, 443, 444, etc |
| Standard | ISO, JIS, ASTM, AS, EN, GB |
| Surface | N0.1, N0.2, N0.3, N0.4, N0.5, N0.6, N0.7, N0.8, 2D, 2B, HL, BA, 6K, 8K, etc |
| Thickness | 0.1-200mm |
| Width | 10-2000mm |
| MOQ | 1MT |
| Packaging | Export standard, seaworthy |
| Trade Term | FOB, CFR, CIF |
| Transport Type | Container, bulk and train |
| Loading port | qingdao, tianjin, etc |
| Payment terms | T/T, L/C at sight,West Union,D/P,D/A,Paypal |
| Delivery time | 15-35 days after confirmed order |
| Chemical composition and mechanical properties of stainless steel coils | |||||||||
Grade |
Chemical Composition (%) | Mechanical Performance | |||||||
| C | Si | Mn | P | S | Ni | Cr | Mo | Hardness | |
| 201 | ≤0.15 | ≤1.00 | 5.5/7.5 | ≤0.060 | ≤0.03 | 3.5/5.5 | 16.0/18.0 | - | HB≤241,HRB≤100, HV≤240 |
| 304 | ≤0.08 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 8.0/11.0 | 18.0/20.0 | - | HB≤187,HRB≤90,HV≤200 |
| 316 | ≤0.08 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 10.0/14.0 | 16.0/18.0 | 2.0/3.0 | HB≤187,HRB≤90,HV≤200 |
| 316L | ≤0.03 | ≤1.00 | ≤2.00 | ≤0.045 | ≤0.03 | 10.0/14.0 | 16.0/18.0 | 2.0/3.0 | HB≤187,HRB≤90,HV≤200 |
| 410 | ≤0.15 | ≤1.00 | ≤1.25 | ≤0.060 | ≤0.03 | ≤0.060 | 11.5/13.5 | - | HB≤183, HRB≤88 HV≤200 |
| 430 | ≤0.12 | ≤1.00 | ≤1.25 | ≤0.040 | ≤0.03 | - | 16.0/18.0 | - | HB≤183, HRB≤88 HV≤200 |
| Finish | Definition | Application |
| 2B | Finished by heat treatment , picking or equipvalent cold rolling , followed by skin pass to obtain adequate luster surface | with bright and smooth surface ,easy for further grinding to obtain brighter surface ,suitable for medical instruments ,milk containers ,tableware |
| BA | bright heat treatment after cold rolling | structual members .etc.kitchen utensil ,cutlery ,eleltric applicances ,medical instruments ,building decorations ,etc. |
| NO.3/NO.4 | polished with No.150-240 abrasives | milky food processing equipment , medicalinstruments ,building decorations |
| HL | finshed by polishing with abrasives of suitable grain size to obtain continuous streaks | building decorations ,such as elevators ,escalators ,door.etc |
| NO.8 | A mirror-like reflective surface ,which is obtained by polishing with successively finer abrasives and buffing extensively with all gritlines are removed |
buliding entrances,bulkding column casting ,elevator's wall * doors ,counters,sculptures |